Media Finish: Gloss
Media Width: 54"
Roll Length: 45m (Full Roll)
Log in to purchase


ICON® 440LSE is a 82 micron flexible white polymeric vinyl film, backed with a highly aggressive pressure sensitive acrylic adhesive system, specifically engineered to adhere to difficult substrates. Suggested application to low surface energy plastics, such as porta-johns, coolers, drums/tanks, powdercoated metals, and most smooth and textured surfaces.


Recommended Uses

Substance Incorporated recommends the following end uses for ICON® 440LSE: Excellent adhesion to a wide variety of smooth and textured HSE/LSE plastics. Graphics and wall murals applied to brick, unsealed concrete, and stucco. Sidewalk and Pavement graphics when combined with ICON® 6100 overlaminate. Permanent adhesion to almost any low surface energy or difficult substrate.



Material 82 micron Polymeric Calendered Vinyl

Colour White
Tensile Strength 63N/25mm

Adhesive Clear Solvent-Based Pressure Sensitive Acrylic
Adhesive Thickness 0.038mm +/-10%
Peel Adhesion 28N/25mm from Stainless Steel
Liner 93LB PE Coated Layflat Paper

Liner Release 30 grams/25mm
Dimensional Stability 0.9 mm
Application Temp. 0°C to 27°C recommended, test prior to specific application
Temperature Range -53°C to 104°C
Shelf Life 2 years when stored at 21°C and 50% relative humidity
Print Compatability Solvent, Eco-Solvent, Latex, UV, and Thermal Transfer Inks
Graphic Life Outdoor durability up to 7 years (unprinted), permanent
Chemical Resistence Resists mild acids, mild akalis, solvents, and salts. Excellent resistance to water, including immersion.



Before applying an overlaminate, allow 24-48 hours for print to dry. Application surface must be free of dust, dirt, debris, grease, and other contaminants. We highly recommend cleaning the installation surface with isopropyl alcohol prior to application. Dry installation is recommended. Due to a highly-aggressive adhesive system, 440LSE will exhibit a slightly higher amount of shrinkage than standard calendered vinyl films.